Modello: P20, 1.2311, 1.2312, 3Cr2Mo
Standard: AiSi, ASTM, bs, DIN, GB, JIS
Luogo D'origine: Cina
Processo Produttivo: Laminati a caldo
Acciaio Speciale: Acciaio per stampi
Tolleranza: ± 1%
Servizio Di Elaborazione: Flessione, Saldatura, Decoiling, Punzonatura, Taglio
| Unità vendibili | : | Ton |
| Esempio immagine | : |
|
The file is encrypted. Please fill in the following information to continue accessing it
Parametri del prodotto
1. Standard internazionale
| GB | DIN | ASIA | JIS |
| 3Cr2MnNi | 1.2311 | P20 | PDS-S |
| 1.2311 | C | Si | Mn | Cr | Mo | S | P |
| 0.35-0.45 | 0.20-0.40 | 0.60-1.00 | 1.80-2.10 | 0.30-0.55 | ≤0.003 | ≤0.003 |
| Flat Bar Size | Round Bar Size(mm) | ||||
| Thickness | Width | Length | Diameter | Length | |
| 10-700 | 155-2200 | 2000-6000 | 20-200 | 2000-6000 | |
4. Tecnica del prodotto:
Introduzione:
Gli acciai per stampo a basso contenuto di carbonio o acciai di gruppo P sono di diversi tipi che includono acciai P2, P3, P4, P5, P6, P20 e P21. Il cromo e il nichel sono i principali elementi di lega che si trovano negli acciai del gruppo P.
Gli acciai per utensili P20 sono nitrossi o carburati. Questi acciai sono in grado di essere lavorati in stampi complessi e grandi. Gli acciai P20 sono utilizzati principalmente in condizioni carbonizzate. La presenza di cromo e nichel migliora la tenacità e la durezza degli acciai P20.
| Tempering: | P20 tool steels are tempered at 482-593°C (900 to 1100°F) for a Rockwell C hardness of 28 to 34. |
| Annealing: | Annealing takes place at 760-788°C (1400 to 1450°F) and then the steels are cooled slowly in the furnace at a temperature less than 4°C (40°F) per hour. |
| Cold Working: | P20 tool steels are capable of being readily cold worked by using conventional tooling methods with the alloy in the annealed condition. |
| Welding: | Conventional methods are used for welding of P20 tool steels. |
| Forging: | P20 tool steels are forged at 1093°C (2000°F) down to 899°C (1650°F). Forging below 871°C (1600°F) is not recommended for these steels. |
| Forming: | P20 tool steels can be readily formed by conventional methods in the annealed condition. |
| Machinability: | P20 tool steels have excellent machinability at about 80% that of water hardening steels. |
| Heat Treatment: | P20 tool steels are heated to 871-899°C (1600-1650°F) in the carburizing medium during the carburizing process. After being carburized, these steels are heated to 816-871°C (1500-1600°F) in order to be hardened and then held for 15 minutes and finally oil quenched. |
| Applications: | P20 tool steels are used for low-temperature applications that include injection molds and die casting dies. |
Fabbrica
Test del prodotto
Imballaggio e spedizione
Contattaci
Se hai qualche domanda, non esitate a contattarmi tramite e -mail o telefono!
Principalmente tubi in acciaio in acciaio a carbone, tubo in acciaio zincato, tubo in acciaio senza cucitura, tubo in acciaio quadrato, tubo in acciaio affinato, tubo in acciaio a forma speciale, filo di ferro zincato e angolo di acciaio, raggio H, acciaio piatto, acciaio rotondo, acciaio a canale, ecc. .
CONTATTACI
Copyright © 2024 Tianjin YF Steel Co., LtdTutti i diritti riservati
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Contact Now